A baseball-bat-like CdTe/TiO2 nanorods-based heterojunction core-shell solar cell

H. Karaagac*, M. Parlak, L. E. Aygun, M. Ghaffari, N. Biyikli, A. K. Okyay

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

14 Atıf (Scopus)

Özet

Rutile TiO2 nanorods on fluorine-doped thin oxide glass substrates via the hydrothermal technique were synthesized and decorated with a sputtered CdTe layer to fabricate a core-shell type n-TiO2/p-CdTe solar cell. Absorbance spectrum verified the absorption contribution of both TiO2 and CdTe to the absorption process. The solar cell parameters, such as open circuit voltage, short circuit current density, fill factor and power conversion efficiency were found to be 0.34 V, 1.27 mA cm-2, 28% and 0.12%, respectively.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)323-326
Sayfa sayısı4
DergiScripta Materialia
Hacim69
Basın numarası4
DOI'lar
Yayın durumuYayınlandı - Ağu 2013
Harici olarak yayınlandıEvet

Finansman

This work was supported in part by European Union Framework Program 7 Marie Curie IRG Grant 239444 and 249196 , COST NanoTP, TUBITAK Grants 109E044 , 112M004 and 112E052 .

FinansörlerFinansör numarası
European Union Framework Program 7 Marie Curie239444, 249196
TUBITAK112E052, 109E044, 112M004

    Parmak izi

    A baseball-bat-like CdTe/TiO2 nanorods-based heterojunction core-shell solar cell' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

    Alıntı Yap