T1 - Reduction behaviors of chromite and nio in liquid FE-C alloys
AU - Uzunoglu, T.
AU - Derin, B.
AU - Yücel, O.
PY - 2007
Y1 - 2007
N2 - In this study, reduction behaviours of Turkish chromite concentrate (48 % Cr 2O 3, 13.30 % FeO, 18.33 % MgO, 12.37 % Al 2O 3, 5.76 % SiO 2) and nickel oxide by Fe-C alloy in graphite crucible were investigated. In the first stage of experiments, steel scraps were melted in graphite crucibles and were saturated with carbon at 1600 °C and 30 min. In the second stage, mixtures of different amount of chromite concentrate, nickel oxide and flux additives (CaO, SiO 2 and CaF 2) were charged into the graphite crucible containing the Fe-C alloy and heated to 1600 °C for different reduction times (0-180 min) under argon gas. The highest Cr and Ni contents in alloys were found as 11.41 and 14.37 % and the highest Cr and Ni recoveries were found as 88 and 94 %, respectively at 180 min.
AB - In this study, reduction behaviours of Turkish chromite concentrate (48 % Cr 2O 3, 13.30 % FeO, 18.33 % MgO, 12.37 % Al 2O 3, 5.76 % SiO 2) and nickel oxide by Fe-C alloy in graphite crucible were investigated. In the first stage of experiments, steel scraps were melted in graphite crucibles and were saturated with carbon at 1600 °C and 30 min. In the second stage, mixtures of different amount of chromite concentrate, nickel oxide and flux additives (CaO, SiO 2 and CaF 2) were charged into the graphite crucible containing the Fe-C alloy and heated to 1600 °C for different reduction times (0-180 min) under argon gas. The highest Cr and Ni contents in alloys were found as 11.41 and 14.37 % and the highest Cr and Ni recoveries were found as 88 and 94 %, respectively at 180 min.
UR - http://www.scopus.com/inward/record.url?scp=84857777202&partnerID=8YFLogxK
M3 - Conference contribution
AN - SCOPUS:84857777202
SN - 9780230630697
T3 - Innovations In The Ferro Alloy Industry - Proceedings of the XI International Conference on Innovations in the Ferro Alloy Industry, Infacon XI
SP - 93
EP - 98
BT - Innovations In The Ferro Alloy Industry - Proceedings of the XI International Conference on Innovations in the Ferro Alloy Industry, Infacon XI
T2 - 11th International Conference on Innovations in the Ferro Alloy Industry, Infacon XI
Y2 - 18 February 2007 through 21 February 2007
ER -