Microstructure and crystallization properties of TeO2-PbF 2 glasses

I. Kabalci*, G. Özen, M. L. Öveçoǧlu

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

17 Citations (Scopus)

Abstract

The microstructures of (1 - x)(TeO2)-xPbF2, (x = 0.1, 0.15, and 0.25 mol) glasses were investigated by using the Raman spectroscopic technique. The effect of compositions on the TeO2 glass networks and the intensity ratios of the deconvoluted Raman peaks were determined. The results confirm that the addition of modifiers to the glass network former shifts the Raman intensity and the peak wavenumber values for each band in the 167-165, 652-645, and 747- 755 cm-1 wavenumber regions. The structural evaluation was recognized from the Raman spectra, with the structural units described as [TeO3+1] polyhedra, [TeO3] trigonal pyramids, and [TeO4] trigonal bipyramids for this binary glass system. Heat-treatment of the samples shows that the metastable crystalline phase of TeO2 known as γ-TeO2 is formed only when the modifier content is 10 mol% in the glass matrix. Transparent glass properties were not realized when the TeO2 amount was decreased to less than 10 mol% content.

Original languageEnglish
Pages (from-to)272-276
Number of pages5
JournalJournal of Raman Spectroscopy
Volume40
Issue number3
DOIs
Publication statusPublished - Mar 2009

Keywords

  • Glass microstructure
  • Raman spectra
  • Tellurite glasses

Fingerprint

Dive into the research topics of 'Microstructure and crystallization properties of TeO2-PbF 2 glasses'. Together they form a unique fingerprint.

Cite this