Effect of calcinated magnesite on rheology of bentonite suspensions. Magnesia-bentonite interaction

Kenan Cinku, Firat Karakas, Feridun Boylu

Research output: Contribution to journalArticlepeer-review

8 Citations (Scopus)

Abstract

In this study, the effect of calcination temperature and time on the structure of calcinated magnesite was investigated. In addition, the effect of calcinated magnesite on rheology when added into bentonite suspension was also examined. Electrokinetic, rheological and stabilization studies including coagulation and gelation tests were performed to explain the mechanism of viscosity increase in bentonite suspension upon addition of the calcinated products. FTIR, SEM, BET analyses and rheological data were used to determine the transition degree of MgCO3 to MgO, and evaluate the structure of MgO and bentonite suspensions. The results from this study showed that specific surface area (SSA) and mean pore radius (MPR) values for the calcinated products were directly affected by the calcination temperature and time. According to the ignition loss and transition ratio from MgCO3 to MgO of the calcinated samples, it was found that the calcination was completed above 800 °C. In order to obtain a bentonite suspension with higher viscosity, interaction of the sufficient amount of MgO particles with bentonite particles were necessary. Based on these results, the formation of gelation and heterocoagulation between MgO and bentonite particles were found to be responsible for these effects.

Original languageEnglish
Pages (from-to)453-466
Number of pages14
JournalPhysicochemical Problems of Mineral Processing
Volume50
Issue number2
DOIs
Publication statusPublished - 2014

Keywords

  • Activation
  • Bentonite
  • Interaction
  • MgCO
  • MgO
  • Viscosity

Fingerprint

Dive into the research topics of 'Effect of calcinated magnesite on rheology of bentonite suspensions. Magnesia-bentonite interaction'. Together they form a unique fingerprint.

Cite this